Material grade: wear-resistant welding wire

Material Identification: High-carbide, high chromium Fe-based alloy

Standard: GB10045-88

Carbon Content: 5.0%

Chromium Content: 28%

Other metal: Mn, Si, etc.

Hardness of the welding wire: HRC58-62

Characteristics:

1, After welding, the reacted compound carbide distributes in the base part of workpiece
2, High anti-wear, generate austenite, welding wire has primary carbide
3, When meet abrasion stress, it is extremely anti-wear
4, It is liable to grinding polish, not suitable for flame cutting or mechanical processing
5, The application temperature should not beyond 550°C

Recommendation:

Suitable for the hard-facing treatment of workpiece that need to endure strong wear and medium impulsive force: welding repair, thermal mill roller/segments repair, cement vertical mill roller/segments, pulverizer roller repair, crush hammer repair, also suitable for manufacturing the composite steel plate and overlaying the composite roller.

Reference standard: BS EN 14700:2005

Specification: Φ2.0mm, Φ2.4mm, Φ2.8mm, Φ3.2mm

Package: cargo in roll: 25KG/roll, 50KG/roll, 200KG/barrel

Welding note: inert gas is not necessary, AC/DC, the arc should be as short as possible